Tesa Double Sided Filmic Tape, 4970, 50MM x 50 Mtrs, Transparent
547176471138
547176471138
Payment Methods Accepted
SUPPLYVANTAGE
Original
Products
Products
Warranty
Against Defects
Against Defects
Returns &
Refund Policy
Refund Policy
Dedicated
Support
Support
100% Client
Protection
Protection
Description
Tesa 4970 is a thick white double-sided self-adhesive tape consisting of a PVC-film backing and a tackified acrylic adhesive.
View AllClose
- Excellent combination of high tack and immediate adhesion
- High coating weight for good bonding performance on rough or dusty surfaces
- Full suitability for long-term applications
- Elongation at break: 20%
- Type of Liner: Glassine
- Colour of Liner: Brown
- Thickness of Liner: 0.71mm
- Weight of Liner: 82 g/mtr sq.
- Adhesion to ABS (after 14 days): 14.4 N/cm, Adhesion to ABS (initial): 13.4 N/cm, Adhesion to Aluminium (after 14 days): 12.6 N/cm, Adhesion to Aluminium (initial): 11.5 N/cm, Adhesion to PC (after 14 days): 16.9 N/cm, Adhesion to PC (initial): 16.2 N/cm
- Adhesion to PE (after 14 days): 9.1 N/cm, Adhesion to PE (initial): 8.5 N/cm, Adhesion to PET (after 14 days): 11.9 N/cm, Adhesion to PET (initial): 11.5 N/cm, Adhesion to PP (after 14 days): 10.8 N/cm, Adhesion to PP (initial): 9.7 N/cm
- Adhesion to PS (after 14 days): 15.2 N/cm, Adhesion to PS (initial): 14.7 N/cm, Adhesion to PVC (after 14 days): 16.6 N/cm, Adhesion to PVC (initial): 12.4 N/cm, Adhesion to Steel (after 14 days): 13.6 N/cm, Adhesion to Steel (initial): 13 N/cm
Item Name: |
Double Sided Filmic Tape |
Manufacturer: |
Tesa |
Color: |
Transparent |
Width: |
50mm |
Adhesive Type: |
Tackified Acrylic |
Length: |
50 Mtrs |
Backing Material: |
PVC |
Thickness (MilliMeters): |
2.25mm |
Temperature Resistance: |
60 to 70 deg.C |
Tensile Strength: |
38 N/cm |
Application: |
Mounting of plastic and wooden trims, Mounting of decorative POS materials and displays, Mounting of signs and scales |