Weicon Anti-Seize High-Tech Assembly Paste, 26100012, 120GM

Anti Seize High-Tech is high temperature resistant, has excellent separating characteristics, is metal-free, neutral to materials and has an NSF approval. Anti-Seize High-Tech is particularly suitable when metal-containing pastes can cause electrolytic reactions, when nickel-containing products should or may not be used due to health reasons and when dark metal containing products should or may not be used for optical reasons.
Surface pre-treatment

Clean and degrease surfaces. Apply the assembly paste evenly. AS is suitable only for assembly paste specific applications, it does not replace pure lubricants and greases.

Processing

Apply a good quantity of Assembly Paste with a brush, cloth or plastic sponge. On threads it is important that Assembly Paste is applied down to the thread root to ensure a good sealing effect. Assembly Paste must not be mixed with greases or oils to avoid changes in the material characteristics. Weicon Assembly Pastes do not replace oil or grease lubrication.

Technical Data:

Basic Oil: Medicinical Oil

Colour: White

Density at +20 Deg.C (+68 Deg.F) (DIN 51757): 1.42 g/cu.cm

OFW device coefficient of friction: 0.10 - 0.13

Friction total: 0.13 µ

Friction thread: 0.11 µ

Friction head bottom: 0.14 µ

VKA-TEST (DIN 51350) goods load: 3.600 N

VKA-TEST (DIN 51350) welding load: 3.800 N

VKA-TEST (DIN 51350) Spherical cap value (1Min/1000N): 0.7mm

Worked penetration ( DIN ISO 2137): 310 - 340 1/10mm

Specific heat transfer capacity (20 Deg.C): 1.574 J/(g·K)

Thermal diffusivity (20 Deg.C): 0.302 sq.mm/s

Thermal conductivity (ISO 22007-4) (20 Deg.C): 0.675 W/m·K

Dielectric strength (DIN EN 60243-1) (20 Deg.C): 6.3 kV/mm

Sulfur content (DIN 514): <0.1%

Water resistance (DIN 51807): 1 - 90

Pressure (DIN 53281-83): 230 N/sq.mm

Salt spray test: >170 h

Specific Resistance: 1.0 x 10^15 Ohm/cm

Temperature Resistance: -40 to +1.400 Deg.C

ISSA-Code: 53.402.81/82/83/84/85/86/87/88/89

IMPA-Code: 450882/83/84/85/86/87

• Reliable protection against corrosion seizing and cold welding
• Metal-free
• NSF approval