Weicon GMK 2510 Contact Adhesive, 16200690, Black, 690GM
(No reviews yet)
Write a Review
- Brand:
- Weicon
- SKU:
- 246923278229
- Minimum Purchase:
- 1 unit
- Item Name:
- Contact Adhesive
- Manufacturer:
- Weicon
- Color:
- Black
- Size:
- 690gm
- Temperature Resistance:
- -40 to +80 Deg.C
- Viscosity:
- 1500 MPa
- Processing Temperature:
- +15 to +35 Deg.C
- Mixing Ratio by Weight:
- 100:7
- Density:
- 0.85 g/cu.cm
- Final Strength:
- 24 hrs
- Storage Stability:
- 12 Months
- Storage Temperature (Degree Celsius):
- +15 to +25 Deg.C
- Evaporation Time:
- 5-15 min.
- Coverage Area:
- 150-300 g/sq.m
- Brand Origin (not manufacture):
- Germany
- Product Size L x B x H (Cms):
- 17.4L x 11.8B x 17.5H
- Delivery Time:
- 2-7 Days
- Unit:
- Set
Description
GMK 2510 is a two-component adhesive based on polychloroprene for full-surface and permanently elastic bonding of parts which are continuously exposed to dynamic loads. The advantage compared to one-component contact adhesives is the considerably better adhesion and the improved temperature resistance. GMK 2510 bonds rubber, metal, textiles, leather, sponge rubber (neoprene), CSM (Hypalon), insulating materials, PU materials with an adhesive coating, wood, stones and many plastics. After curing the bonding is moisture-proof. Weicon GMK 2510 is not suitable for materials such as polystyrene foam, polyethylene, polypropylene parts, PVC soft foam and PVC imitation leather.
View AllClose
- Permanently elastic
- Temperature-resistant
- Strong
Item Name: |
Contact Adhesive |
Manufacturer: |
Weicon |
Color: |
Black |
Size: |
690gm |
Temperature Resistance: |
-40 to +80 Deg.C |
Viscosity: |
1500 MPa |
Processing Temperature: |
+15 to +35 Deg.C |
Mixing Ratio by Weight: |
100:7 |
Density: |
0.85 g/cu.cm |
Final Strength: |
24 hrs |
Storage Stability: |
12 Months |
Storage Temperature (Degree Celsius): |
+15 to +25 Deg.C |
Evaporation Time: |
5-15 min. |
Coverage Area: |
150-300 g/sq.m |
Brand Origin (not manufacture): |
Germany |
Product Size L x B x H (Cms): |
17.4L x 11.8B x 17.5H |
Delivery Time: |
2-7 Days |
Unit: |
Set |
Related Products
Weicon
AED197.00
GMK 2510 is a two-component adhesive based on polychloroprene for full-surface and permanently elastic bonding of parts which are continuously exposed to dynamic loads. The advantage compared to...
Weicon
AED84.00
GMK 2410 is based on polychloroprene (CR) for the high-strength, full-surface and flexible bonding of: rubber to rubber, rubber to metal. Weicon GMK 2410 also bonds cellular rubber (e.g. neoprene),...
Available on Request
Weicon
GMK 2410 is based on polychloroprene (CR) for the high-strength, full-surface and flexible bonding of: rubber to rubber, rubber to metal. Weicon GMK 2410 also bonds cellular rubber (e.g. neoprene),...
Weicon
AED90.00
GMK 2410 is based on polychloroprene (CR) for the high-strength, full-surface and flexible bonding of: rubber to rubber, rubber to metal. Weicon GMK 2410 also bonds cellular rubber (e.g. neoprene),...
Weicon
AED48.00
Weicon Contact VA 1401 has medium viscosity (100-150 mPa.s) and hardens quickly. It shows good results on fabric, paper, cardboard, cartons, foam rubber and large-pored elastomers. VA 1401 is a...
Weicon
AED39.00
Weicon Contact VM 20 has a low viscosity (20-40 mPa) and hardens very quickly. It is suited for all types of metal bonds, especially for the bonding of precisely fitted parts in serial production. VM...
Weicon
AED1,216.00
VA 250 Black is highly viscous (2000-3000 mPa) and temperature resistant between -50 and +140 degree celsius. It hardens slowly and with residual elasticity, is rubber-filled and black, and has high...
Weicon
AED102.00
Weicon Contact VA 30 Black has medium viscosity (300 mPa) and is temperature resistant between -50 and +140 degree celsius. It has a longer curing time, is rubber-filled and black, hardens with...
Weicon
AED102.00
VA 250 Black is highly viscous (2000-3000 mPa) and temperature resistant between -50 and +140 degree celsius. It hardens slowly and with residual elasticity, is rubber-filled and black, and has high...