Weicon C Epoxy Resin, 10100005, 0.5 Kg

(No reviews yet) Write a Review
Brand:
Weicon
SKU:
816374591345
Minimum Purchase:
1 unit
Item Name:
Epoxy Resin
Manufacturer:
Weicon
Size:
0.5 Kg
Application Area:
Tool and Mould Making sector, as well as in many other industrial areas subjected to high thermal stress
Curing Time:
10 hrs
Viscosity:
25000 MPa
Tensile Strength:
48 MPa
Hardness:
84 +/-3
Elongation at Break:
0.9%
Processing Temperature:
+15 to 40 Deg.C
Mixing Ratio by Weight:
100:8
Mixing Ratio by Volume:
100:14
Density:
1.6 g/cu.cm
Max. Layer Thickness:
60mm
Temperature Resistance:
-35 to +200 Deg.C
Heating Capacity:
0.90 J
Thermal Conductivity:
0.6 W/mK
Final Strength:
24 hrs
Compressive Strength:
140 MPa
Color After Curing:
Grey
Impact Strength:
8-9 kJ/sq.m
Bending Strength:
77 MPa
Adhesion Strength:
16 MPa
Brand Origin (not manufacture):
Germany
Product Size L x B x H (Cms):
19.4L x 11B x 11.8H
Delivery Time:
2-7 Days
Unit:
Piece
See Full Product Specs
AED229.00

Description

Temperature resistant and liquid epoxy resin system, specially for the industrial use. Non-corrosive, anti-magnetic, cures practically without shrinkage. Weicon C is particularly suitable as an adhesive for large-scale applications, for pouring out moulds and for the production of fixing devices and tools (e.g. injection moulds). It can be used in the tool and mould making sector, as well as in many other industrial areas subjected to high thermal stress.
  • Aluminium-filled
  • Up to +220 Deg.C (+428 Deg.F) high temperature resistant
Item Name:
Epoxy Resin
Manufacturer:
Weicon
Size:
0.5 Kg
Application Area:
Tool and Mould Making sector, as well as in many other industrial areas subjected to high thermal stress
Curing Time:
10 hrs
Viscosity:
25000 MPa
Tensile Strength:
48 MPa
Hardness:
84 +/-3
Elongation at Break:
0.9%
Processing Temperature:
+15 to 40 Deg.C
Mixing Ratio by Weight:
100:8
Mixing Ratio by Volume:
100:14
Density:
1.6 g/cu.cm
Max. Layer Thickness:
60mm
Temperature Resistance:
-35 to +200 Deg.C
Heating Capacity:
0.90 J
Thermal Conductivity:
0.6 W/mK
Final Strength:
24 hrs
Compressive Strength:
140 MPa
Color After Curing:
Grey
Impact Strength:
8-9 kJ/sq.m
Bending Strength:
77 MPa
Adhesion Strength:
16 MPa
Brand Origin (not manufacture):
Germany
Product Size L x B x H (Cms):
19.4L x 11B x 11.8H
Delivery Time:
2-7 Days
Unit:
Piece