Weicon HP Epoxy Resin, 10390002, 0.2 Kg
- Brand:
- Weicon
- SKU:
- 711935792922
- Minimum Purchase:
- 1 unit
- Item Name:
- Epoxy Resin
- Manufacturer:
- Weicon
- Size:
- 0.2 Kg
- Application Area:
- Wet and damp surfaces and in underwater applications
- Curing Time:
- 12 hrs
- Viscosity:
- 550000 MPa
- Tensile Strength:
- 31 MPa
- Hardness:
- 75 +/-3
- Elongation at Break:
- 9%
- Processing Temperature:
- +15 to 40 Deg.C
- Mixing Ratio by Weight:
- 100:83
- Mixing Ratio by Volume:
- 100:95
- Density:
- 1.5 g/cu.cm
- Max. Layer Thickness:
- 10mm
- Temperature Resistance:
- -35 to +160 Deg.C
- Final Strength:
- 36 hrs
- Compressive Strength:
- 65 MPa
- Color After Curing:
- White
- Impact Strength:
- 21 kJ/sq.m
- Bending Strength:
- 50 MPa
- Adhesion Strength:
- 25 MPa
- Brand Origin (not manufacture):
- Germany
- Product Size L x B x H (Cms):
- 19.4L x 11B x 11.8H
- Delivery Time:
- 2-7 Days
- Unit:
- Piece
Description
Weicon HP is a 2-component epoxy resin with longer curing time, enormous shock resistance as well as high residual elasticity and abrasion resistance. Due to its high elongation at break and paste-like texture, Weicon HP can be used for repairs, as abrasion protection as well as for lining heavily stressed equipment. The adhesive also shows excellent adhesion to wet and damp surfaces and in underwater applications.
View AllClose
- Pasty
- Mineral-filled
- Shock-resistant
- Cures under water as well as on wet and damp surfaces
Item Name: |
Epoxy Resin |
Manufacturer: |
Weicon |
Size: |
0.2 Kg |
Application Area: |
Wet and damp surfaces and in underwater applications |
Curing Time: |
12 hrs |
Viscosity: |
550000 MPa |
Tensile Strength: |
31 MPa |
Hardness: |
75 +/-3 |
Elongation at Break: |
9% |
Processing Temperature: |
+15 to 40 Deg.C |
Mixing Ratio by Weight: |
100:83 |
Mixing Ratio by Volume: |
100:95 |
Density: |
1.5 g/cu.cm |
Max. Layer Thickness: |
10mm |
Temperature Resistance: |
-35 to +160 Deg.C |
Final Strength: |
36 hrs |
Compressive Strength: |
65 MPa |
Color After Curing: |
White |
Impact Strength: |
21 kJ/sq.m |
Bending Strength: |
50 MPa |
Adhesion Strength: |
25 MPa |
Brand Origin (not manufacture): |
Germany |
Product Size L x B x H (Cms): |
19.4L x 11B x 11.8H |
Delivery Time: |
2-7 Days |
Unit: |
Piece |
Related Products
Weicon
AED123.00
Weicon A has a DNV GL-certificate and is specially suitable for repair work in the marine industry. It can be used to remove corrosion damages and pitting on tanks, to repair pipes and castings as...
Weicon
AED168.00
Weicon F is particularly suited for applications on components made from aluminium, aluminium alloys, magnesium and other light metals. Weicon F can be used for inexpensive repairs of all types, for...
Weicon
AED179.00
Weicon BR is particularly suited for filling in blowholes and for repairing and rebuilding bronze equipment parts and castings. It can be used in tool construction, model and mould making, and in...
Weicon
AED250.00
Weicon F2 is suited for the casting of models, moulds and templates, for the repair of porous and damaged castings, for the production of prototypes and holding devices, and for pouring out swages to...
Weicon
AED162.00
WEICON SF is particularly suited for quick repairs and the reconditioning of leaky pipelines, housings and gears, for anchorages, and for the production of fixing devices. WEICON SF can be used in...
Weicon
AED247.00
Weicon Ceramic BL is liquid, brushable, filled with silicium carbide and zirconium silicate, temperature resistant up to +180 Deg.C and resistant to chemicals. It offers extreme wear protection and...
Weicon
AED233.00
Weicon Ceramic W is pasty, mineral-filled, temperature-resistant up to +150 degree celsius (briefly up to +260 degree celsius) and resistant to chemicals. It offers high wear protection and abrasion...
Weicon
AED179.00
Weicon Plastic Metal type HB 300 is pasty, steel-filled and high temperature resistant up to +200 degree celsius (briefly up to +280 degree celsius). It is processed with a mixing ratio of 1:1...
Weicon
AED148.00
Weicon WR is suitable for areas where metal parts are subject to heavy wear due to friction. For example, the epoxy resin system can be used for repairs and for casting around shafts, for casting...